JPFL Films Private Limited

Milky White Films

Product Table / Data Sheet

 

Type Description Standard Thickness* (µ) USP Application PDF
J-470 Milky white, untreated plain bi-axially oriented polyester film 75,100,125,190,225,250,300,350 µ
  • Tough Flexibility to Prevent Delamination
  • Good Insulation Property
  • Excellent Machinability
  • Excellent Mechanical Properties
  • Excellent Dimensional Stability
 Insulation in rotating electrical machine, printing, other general purpose & industrial applications,  
J-481 Milky white, One side antistatic treated bi-axially oriented polyester film 125,190,225,250,300,350 µ
  • Excellent Antistatic Property on Coated Side
  • Tough Flexibility to Prevent Delamination
  • Good Insulation Property
  • Excellent Machinability
  • Excellent Mechanical Properties
  • Excellent Dimensional Stability
 Insulation in rotating electrical machine, printing, other general purpose & industrial applications,  
J-482 Milky white, Both side antistatic treated bi-axially oriented polyester film 125,190,225,250,300,350 µ
  • Excellent Antistatic Property both Side
  • Tough Flexibility to Prevent Delamination
  • Good Insulation Property
  • Excellent Machinability
  • Excellent Mechanical Properties
  • Excellent Dimensional Stability
 Insulation in rotating electrical machine, printing, other general purpose & industrial applications,  

THERMAL GLOSS FINISH BOPP FILM

Application:

Insulation in rotating electrical machine, printing, other general purpose & industrial applications,

Description:

Milky white, untreated plain bi-axially oriented polyester film

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
J-470
Milky white, untreated plain bi-axially oriented polyester film
Insulation in rotating electrical machine, printing, other general purpose & industrial applications, Co-extruded tough milky white polyester film having excellent surface and good electrical property

THERMAL GLOSS FINISH BOPP FILM

Application:

Insulation in rotating electrical machine, printing, other general purpose & industrial applications,

Description:

Milky white, One side antistatic treated bi-axially oriented polyester film

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
J-481
Milky white, One side antistatic treated bi-axially oriented polyester film
Insulation in rotating electrical machine, printing, other general purpose & industrial applications, Co-extruded tough milky white polyester film having excellent surface and good electrical property

THERMAL GLOSS FINISH BOPP FILM

Application:

Insulation in rotating electrical machine, printing, other general purpose & industrial applications,

Description:

Milky white, Both side antistatic treated bi-axially oriented polyester film

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
J-482
Milky white, Both side antistatic treated bi-axially oriented polyester film
Insulation in rotating electrical machine, printing, other general purpose & industrial applications, Co-extruded tough milky white polyester film having excellent surface and good electrical property
 