METALLIZED

Product Table / Data Sheet

 

Type Description Standard Thickness* (µ) USP Application PDF
CPH1-MD It is a co-extruded, one side Heat Sealable, other side vacuum deposited aluminum, barrier Cast Polypropylene (CPP) Film. 20,22,25,30,35,40,50 µ
  • Good barrier properties
  • Brilliant metal appearance
  • High seal strength
  • Heat sealable on the non-metallised surface with excellent hot tack
 Packaging & conversion,Typically laminated on the metallised side with BOPP, Candy packaging  
CPH1-LSMD It is a co-extruded, one side Heat Sealable, other side vacuum deposited aluminum, barrier Cast Polypropylene (CPP) Film. 20,22,25,30,35,40 µ
  • Good barrier properties
  • Low Seal Initiation Temperature
  • Brilliant metal appearance
  • High seal strength
  • Heat sealable on the non-metallised surface with excellent hot tack
 Typically laminated on the metallised side with BOPP/BOPET, Biscuits & Snacks Packaging  
CPH1-LSIMD It is a co-extruded, one side Heat Sealable, other side vacuum deposited aluminum, barrier Cast Polypropylene (CPP) Film. 15,18,20,22,25,30,35,40 µ
  • Good barrier properties
  • Low Seal Initiation Temperature
  • Brilliant metal appearance
  • High seal strength
  • Heat sealable on the non-metallised surface with excellent hot tack
 Typically laminated on the metallised side with BOPP/BOPET, Biscuits & Snacks Packaging  
CPH1-EMD It is a co-extruded, one side Heat Sealable, other side vacuum deposited aluminum, barrier Cast Polypropylene (CPP) Film. 20,22,25,30,35,40,50 µ
  • Good barrier properties
  • Brilliant metal appearance
  • High seal strength
  • Heat sealable on the non-metallised surface with excellent hot tack
 Packaging & conversion, Suitable for Extrusion Lamination Process  
CPH1-MDHB It is a co-extruded, one side Heat Sealable, Other side vacuum deposited aluminum, high barrier Cast Polypropylene (CPP) Film. 20,22,25 µ
  • Excellent barrier properties (Gas, moisture & light)
  • Low SIT in comparison with normal metallised CPP film
  • Heat sealable on the non-metallised surface with excellent hot tack
  • High seal strength
 Packaging & conversion – Chips, snacks & bakery products, Typically laminated on the metallised side with PET/BOPP, Suitable for gas (N2) flush packaging.  

THERMAL GLOSS FINISH BOPP FILM

Application:

Packaging & conversion,Typically laminated on the metallised side with BOPP, Candy packaging

Description:

It is a co-extruded, one side Heat Sealable, other side vacuum deposited aluminum, barrier Cast Polypropylene (CPP) Film.

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
CPH1-MD
It is a co-extruded, one side Heat Sealable, other side vacuum deposited aluminum, barrier Cast Polypropylene (CPP) Film.
Packaging & conversion,Typically laminated on the metallised side with BOPP, Candy packaging

THERMAL GLOSS FINISH BOPP FILM

Application:

Typically laminated on the metallised side with BOPP/BOPET, Biscuits & Snacks Packaging

Description:

It is a co-extruded, one side Heat Sealable, other side vacuum deposited aluminum, barrier Cast Polypropylene (CPP) Film.

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
CPH1-LSMD
It is a co-extruded, one side Heat Sealable, other side vacuum deposited aluminum, barrier Cast Polypropylene (CPP) Film.
Typically laminated on the metallised side with BOPP/BOPET, Biscuits & Snacks Packaging

THERMAL GLOSS FINISH BOPP FILM

Application:

Typically laminated on the metallised side with BOPP/BOPET, Biscuits & Snacks Packaging

Description:

It is a co-extruded, one side Heat Sealable, other side vacuum deposited aluminum, barrier Cast Polypropylene (CPP) Film.

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
CPH1-LSIMD
It is a co-extruded, one side Heat Sealable, other side vacuum deposited aluminum, barrier Cast Polypropylene (CPP) Film.
Typically laminated on the metallised side with BOPP/BOPET, Biscuits & Snacks Packaging

THERMAL GLOSS FINISH BOPP FILM

Application:

Packaging & conversion, Suitable for Extrusion Lamination Process

Description:

It is a co-extruded, one side Heat Sealable, other side vacuum deposited aluminum, barrier Cast Polypropylene (CPP) Film.

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
CPH1-EMD
It is a co-extruded, one side Heat Sealable, other side vacuum deposited aluminum, barrier Cast Polypropylene (CPP) Film.
Packaging & conversion, Suitable for Extrusion Lamination Process

THERMAL GLOSS FINISH BOPP FILM

Application:

Packaging & conversion – Chips, snacks & bakery products, Typically laminated on the metallised side with PET/BOPP, Suitable for gas (N2) flush packaging.

Description:

It is a co-extruded, one side Heat Sealable, Other side vacuum deposited aluminum, high barrier Cast Polypropylene (CPP) Film.

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
CPH1-MDHB
It is a co-extruded, one side Heat Sealable, Other side vacuum deposited aluminum, high barrier Cast Polypropylene (CPP) Film.
Packaging & conversion – Chips, snacks & bakery products, Typically laminated on the metallised side with PET/BOPP, Suitable for gas (N2) flush packaging.
 

About Us

Applications

Products

Other Links

E-Sales

*Disclosure: Formerly a Division of Jindal Poly Films Limited.

Follow Us On