Transparent Non Heat Sealable

Product Table / Data Sheet

 

Type Description Standard Thickness* (µ) USP Application PDF
N1 Transparent Non Heat Sealable One Side Corona Treated 8 to 50 µ
  • High Surface Gloss and Transparency
  • Excellent Clarity
  • Excellent Surface Treatment Retention
  • Excellent Anchorage of Inks and Lamination Adhesive on Treated Side
  • Excellent Machinability
  • Very Good Barrier Properties
  • Suitable for Various Printing / Lamination Machines
Book Covers Etc. This Film Is Also Suitable for Cold Seal Application.  
N2 Transparent Non Heat Sealable Both Side Corona Treated 8 to 50 µ
  • High Surface Gloss and Transparency
  • Excellent Clarity
  • Excellent Surface Treatment Retention
  • Excellent Anchorage of Inks and Lamination Adhesive
  • Excellent Machinability
  • Very Good Barrier Properties
  • Suitable for Various Printing / Lamination Machines
Reverse Printing and Lamination for Packaging Applications, Lamination of Printed Paper Boards / Posters / Book Covers Etc.  
N1-AT Transparent Non Heat Sealable One Side Corona Treated 20 TO 50 µ
  • High Surface Gloss
  • Excellent Surface Treatment Retention
  • Excellent Anchorage of Various Pressure Sensitive Adhesives on Treated Side
  • Excellent Machinability
  • Excellent Mechanical Properties
PRESSURE SENSITIVE ADHESIVE TAPE  
N1-BG Transparent Non Heat Sealable One Side Corona Treated 20 TO 50 µ
  • High Surface Gloss
  • Excellent Clarity
  • Excellent Surface Treatment Retention
  • Excellent Anchorage of Inks on Treated Side
  • Excellent Machinability
  • Excellent Mechanical Properties
  • Excellent Dimensional Stability
Textile Bag Application  
N1-TFT Transparent Non Heat Sealable One Side Flame Treated Side Corona Treated 20 TO 50 µ
  • High Surface Gloss
  • Excellent Surface Treatment Retention
  • Excellent Anchorage of Various Pressure Sensitive Adhesives on Treated Side
  • 100% Back Treatment Free
  • Excellent Machinability
  • Excellent Mechanical Properties
  • Excellent Dimensional Stability
Pressure Sensitive Adhesive Tape  
N0 Transparent Non Heat Sealable Untreated Release 12 TO 35 µ
  • High Surface Gloss
  • Excellent Antistatic Characteristics
  • Moderate Slip
  • Very Good Smooth Surface for Protecting Scratches on Laminates
  • Untreated Surface for Preventing Sticking Between Laminates
  • Excellent Dimensional Stability
Release Liner for Decorative Laminates  
N1 -LB Transparent High Glossy High Energy Treated 25 TO 50 µ
  • Excellent Clarity
  • Excellent Surface Gloss
  • Low Haze
  • Specially Design for Surface Printing Applications
  • Excellent Anchorage and Get up of Inks on High Glossy High Energy Treated Side
  • Excellent Anchorage of Hot Melt Adhesive on Other Side
  • Excellent Machinability
  • Suitable for Various Printing / Lamination Machines
Wrap Around and Pressure Sensitive Label Applications  
N2-LB Transparent High Glossy High Energy Treated 25 TO 50 µ
  • Excellent Clarity
  • Excellent Surface Gloss
  • Low Haze
  • Specially Design for Surface Printing Applications
  • Excellent Anchorage and Get up of Inks on High Glossy High Energy Treated Side
  • Excellent Anchorage of Hot Melt and Pressure Sensitive Adhesive on Other Side
  • Excellent Machinability
  • Suitable for Various Printing / Lamination Machines
Wrap Around and Pressure Sensitive Label Applications  
N1-HCF Transparent Non Heat Sealable One Side Corona Treated – Anti slip 15 to 20 µ
  • High Surface Gloss
  • Excellent Surface Treatment Retention
  • Excellent bond in Extrusion lamination at Treated Side
  • Excellent Machinability
  • Excellent Mechanical Properties
  • Excellent Dimensional Stability
Suitable for Extrusion Lamination with PP Woven Fabric; where Other Side is modified with Anti-Slip / Anti-Skid Property  
SM1 Transparent One Side Non Heat Sealable Other Side Corona Treated -Modified Layer 10 to 30 µ
  • High Surface Gloss and Transparency
  • Very Good Barrier Properties
  • Excellent Slip and Antistatic Properties
  • Excellent Surface Treatment Retention and Adhesion to Inks & Adhesives
  • Excellent Machinability
  • Excellent Mechanical Properties
  • Excellent Dimensional Stability
For Single / Two Ply Printing, Lamination and Flower Wrap Application  
N1-LH Transparent Non Heat Sealable One Side Corona Treated Low Haze 17 TO 50 µ
  • Low Haze
  • Excellent Surface Gloss and Transparency
  • Excellent Surface Treatment Retention
  • Excellent Adhesion of Holographic Coating and Printing Inks on Treated Side
  • Water Clear Holographic Appearance after Embossing
  • Excellent Machinability
  • Excellent Mechanical Properties
  • Excellent Dimensional Stability
Low Haze Base Film for Holography Embossing, Textile Bags and Flower Overwrap Applications  

THERMAL GLOSS FINISH BOPP FILM

Application:

Book Covers Etc. This Film Is Also Suitable for Cold Seal Application.

Description:

Transparent Non Heat Sealable One Side Corona Treated

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
N1
Transparent Non Heat Sealable One Side Corona Treated
Book Covers Etc. This Film Is Also Suitable for Cold Seal Application. Transparent, Non Heat Sealable, One Side Corona Treated, High Glossy OPP Film with Excellent Clarity, Slip and Antistatic Properties for use in Printing and Lamination Application. The Corona treated side is specifically designed for Excellent Adhesion of Inks and Lamination Adhesives.

THERMAL GLOSS FINISH BOPP FILM

Application:

Reverse Printing and Lamination for Packaging Applications, Lamination of Printed Paper Boards / Posters / Book Covers Etc.

Description:

Transparent Non Heat Sealable Both Side Corona Treated

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
N2
Transparent Non Heat Sealable Both Side Corona Treated
Reverse Printing and Lamination for Packaging Applications, Lamination of Printed Paper Boards / Posters / Book Covers Etc. Transparent, Non Heat Sealable, Both Side Corona Treated, High Glossy OPP Film with Excellent Clarity, Slip and Antistatic Properties for use in Printing and Lamination Application. The Corona treated sides are specifically designed for Excellent Adhesion of Inks and Lamination Adhesives

THERMAL GLOSS FINISH BOPP FILM

Application:

PRESSURE SENSITIVE ADHESIVE TAPE

Description:

Transparent Non Heat Sealable One Side Corona Treated

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
N1-AT
Transparent Non Heat Sealable One Side Corona Treated
PRESSURE SENSITIVE ADHESIVE TAPE Transparent, Non Heat Sealable, One Side Corona Treated,

THERMAL GLOSS FINISH BOPP FILM

Application:

Textile Bag Application

Description:

Transparent Non Heat Sealable One Side Corona Treated

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
N1-BG
Transparent Non Heat Sealable One Side Corona Treated
Textile Bag Application Transparent, Non Heat Sealable, One Side Corona Treated, High Glossy OPP Film for use in Textile Bag Application. The Corona treated side is specifically designed for surface Printing and Excellent anchorage of Inks. Film is designed for Excellent Machinability during printing and bag making process.

THERMAL GLOSS FINISH BOPP FILM

Application:

Pressure Sensitive Adhesive Tape

Description:

Transparent Non Heat Sealable One Side Flame Treated Side Corona Treated

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
N1-TFT
Transparent Non Heat Sealable One Side Flame Treated Side Corona Treated
Pressure Sensitive Adhesive Tape Transparent, Non Heat Sealable, One Side Flame Treated, High Glossy OPP Film for use in Pressure Sensitive Adhesive Tape Manufacturing Application. The flame treated surface is specifically designed for excellent anchorage of various solvent and water based pressure sensitive adhesive used for self adhesive tape manufacturing. Untreated side is 100% back treatment free, which facilitate the trouble free unwinding of adhesive coated jumbo rolls.

THERMAL GLOSS FINISH BOPP FILM

Application:

Release Liner for Decorative Laminates

Description:

Transparent Non Heat Sealable Untreated Release

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
N0
Transparent Non Heat Sealable Untreated Release
Release Liner for Decorative Laminates Transparent, Non Heat Sealable, Untreated, High Glossy OPP Film with Excellent Clarity and Antistatic Property for use in Release Lining Application for Decorative Laminate Manufacturing. The surface of the film is specifically designed for providing very easy release between the decorative laminates as well as protecting the laminate surface for developing scratches during crosslinking stage.

THERMAL GLOSS FINISH BOPP FILM

Application:

Wrap Around and Pressure Sensitive Label Applications

Description:

Transparent High Glossy High Energy Treated

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
N1 -LB
Transparent High Glossy High Energy Treated
Wrap Around and Pressure Sensitive Label Applications Transparent, Non Heat Sealable, High Glossy High Energy Treated OPP Film with excellent clarity, slip and antistatic properties for use in various label application. One side is high glossy high energy treated surface, specifically designed for excellent get up and adhesion of surface printing by flexo / gravure process. Other Side is design for anchorage with hot melt adhesives

THERMAL GLOSS FINISH BOPP FILM

Application:

Wrap Around and Pressure Sensitive Label Applications

Description:

Transparent High Glossy High Energy Treated

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
N2-LB
Transparent High Glossy High Energy Treated
Wrap Around and Pressure Sensitive Label Applications Transparent, Non Heat Sealable, High Glossy High Energy Treated OPP Film with excellent clarity, slip and antistatic properties for use in various label application. One side is high glossy high energy treated surface, specifically designed for excellent get up and adhesion of surface printing by flexo / gravure process. Other Side is treated for facilitating anchorage with various hot melt and pressure sensitive adhesives.

THERMAL GLOSS FINISH BOPP FILM

Application:

Suitable for Extrusion Lamination with PP Woven Fabric; where Other Side is modified with Anti-Slip / Anti-Skid Property

Description:

Transparent Non Heat Sealable One Side Corona Treated – Anti slip

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
N1-HCF
Transparent Non Heat Sealable One Side Corona Treated – Anti slip
Suitable for Extrusion Lamination with PP Woven Fabric; where Other Side is modified with Anti-Slip / Anti-Skid Property Transparent, Non Heat Sealable, One Side Corona Treated, High Glossy OPP Film for Extrusion lamination with PP woven fabric. The corona treated surface is specifically designed to suit extrusion lamination process. Untreated side is modified with anti-slip / anti-skid property

THERMAL GLOSS FINISH BOPP FILM

Application:

For Single / Two Ply Printing, Lamination and Flower Wrap Application

Description:

Transparent One Side Non Heat Sealable Other Side Corona Treated -Modified Layer

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
SM1
Transparent One Side Non Heat Sealable Other Side Corona Treated -Modified Layer
For Single / Two Ply Printing, Lamination and Flower Wrap Application Transparent, One side Non Heat Sealable other side corona treated modified layer suitable for single/two ply Printing, lamination and flower wrap application

THERMAL GLOSS FINISH BOPP FILM

Application:

Low Haze Base Film for Holography Embossing, Textile Bags and Flower Overwrap Applications

Description:

Transparent Non Heat Sealable One Side Corona Treated Low Haze

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
N1-LH
Transparent Non Heat Sealable One Side Corona Treated Low Haze
Low Haze Base Film for Holography Embossing, Textile Bags and Flower Overwrap Applications Transparent, Low Haze, Non Heat Sealable, One Side Corona Treated OPP Base Film for Holography Embossing Textile Bags And Flower Overwrap Applications. The corona treated side is specifically designed for excellent adhesion of holographic coating and printing inks. Because of very low haze of the film, water clear holographic appearance exhibited by the film after embossing. High clarity and low haze of the film impart excellent aesthetic appeal for textile bags and flower overwrapping.