JPFL Films Private Limited

White Opaque Films

Product Table / Data Sheet

 

Type Description Standard Thickness* (µ) USP Application PDF
J-600 Opaque white, untreated plain bi-axially oriented polyester film 50,75,100,125,150,175,250 µ
  • High Opacity
  • Excellent Machinability
  • Excellent Mechanical Properties
  • Excellent Dimensional Stability
 Label printing, Photographic printing, coating & other general-purpose applications  
J-604 Opaque white, One side corona treated bi-axially oriented polyester film 50,75,100,125,150,175,250 µ
  • High Opacity
  • High Surface Gloss
  • Excellent Machinability
  • Excellent Mechanical Properties
  • Excellent Dimensional Stability
  • Improved Adhesion Properties
 Label printing, Photographic printing, coating & other general-purpose applications  
J-605 Opaque white, untreated plain with rough surface, Biaxially oriented polyester film 50,75 µ
  • High Opacity
  • High Gloss
  • Excellent Machinability
  • Excellent Mechanical Properties
  • Excellent Dimensional Stability
 Label printing, Photographic printing, coating and other general-purpose applications.  
J-611 Opaque white, one side chemically treated bi-axially oriented polyester film 50,75,125,175,250 µ
  • High Opacity
  • Excellent Adhesion to Solvent base Ink on Coated Side
  • High Surface Gloss
  • Excellent Machinability
  • Excellent Mechanical Properties
  • Excellent Dimensional Stability
 Label printing, Photographic printing, coating & other general-purpose applications  
J-612 Opaque white, both side chemically treated bi-axially oriented polyester film 50,75,125,175,190,250 µ
  • High Opacity
  • Excellent Adhesion to Solvent base Ink both Sides
  • High Surface Gloss
  • Excellent Machinability
  • Excellent Mechanical Properties
  • Excellent Dimensional Stability
 Label printing, Photographic printing, coating & other general-purpose applications  
J-632 Semi opaque white with both side antistatic-coated 125 µ
  • Excellent Antistatic Property
  • Excellent Machinability
  • Excellent Dimensional Stability
 Film suitable for Labels, cards, printing and other general application  

THERMAL GLOSS FINISH BOPP FILM

Application:

Label printing, Photographic printing, coating & other general-purpose applications

Description:

Opaque white, untreated plain bi-axially oriented polyester film

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
J-600
Opaque white, untreated plain bi-axially oriented polyester film
Label printing, Photographic printing, coating & other general-purpose applications White opaque polyester film having smooth surface, excellent superior gloss, high opacity and good handling property

THERMAL GLOSS FINISH BOPP FILM

Application:

Label printing, Photographic printing, coating & other general-purpose applications

Description:

Opaque white, One side corona treated bi-axially oriented polyester film

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
J-604
Opaque white, One side corona treated bi-axially oriented polyester film
Label printing, Photographic printing, coating & other general-purpose applications White opaque polyester film having smooth surface, excellent superior gloss, high opacity and good handling property

THERMAL GLOSS FINISH BOPP FILM

Application:

Label printing, Photographic printing, coating and other general-purpose applications.

Description:

Opaque white, untreated plain with rough surface, Biaxially oriented polyester film

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
J-605
Opaque white, untreated plain with rough surface, Biaxially oriented polyester film
Label printing, Photographic printing, coating and other general-purpose applications. White opaque polyester film having slight rougher surface, high opacity and good handling property

THERMAL GLOSS FINISH BOPP FILM

Application:

Label printing, Photographic printing, coating & other general-purpose applications

Description:

Opaque white, one side chemically treated bi-axially oriented polyester film

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
J-611
Opaque white, one side chemically treated bi-axially oriented polyester film
Label printing, Photographic printing, coating & other general-purpose applications White opaque, one side chemically coated, other side plain polyester film having smooth surface, excellent superior gloss, high opacity and good handling property

THERMAL GLOSS FINISH BOPP FILM

Application:

Label printing, Photographic printing, coating & other general-purpose applications

Description:

Opaque white, both side chemically treated bi-axially oriented polyester film

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
J-612
Opaque white, both side chemically treated bi-axially oriented polyester film
Label printing, Photographic printing, coating & other general-purpose applications White opaque, both side chemically coated polyester film having smooth surface, superior gloss,high opacity and good handling property

THERMAL GLOSS FINISH BOPP FILM

Application:

Film suitable for Labels, cards, printing and other general application

Description:

Semi opaque white with both side antistatic-coated

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
J-632
Semi opaque white with both side antistatic-coated
Film suitable for Labels, cards, printing and other general application Semi-opaque white with both side antistatic-coated polyester film having smooth surface and good handling property
 

About Us

Applications

Products

Other Links

E-Sales

*Disclosure: Formerly a Division of Jindal Poly Films Limited.

Follow Us On