JPFL Films Private Limited

Hazy Films

Product Table / Data Sheet

 

Type Description Standard Thickness* (µ) USP Application PDF
J-400 J-400 grade of polyester film is a hazy and both side untreated bi-axially oriented polyester film. 19,23,30,36,50,75,100,125,175,190,250 µ
  • Good Transparency
  • Good Insulation Property
  • Excellent Machinability
  • Excellent Mechanical Properties
  • Excellent Dimensional Stability
 • Electrical applications (wire and cable insulation) • General purpose use and other industrial applications  
J-403 co extruded transparent corona treated polyester film having excellent surface and good handling property. And Treated side wound inside. 75,100,125,190,250 µ
  • Improved Adhesion Properties on Corona Treated Side
  • Good Insulation Property
  • Excellent Machinability
  • Excellent Mechanical Properties
  • Excellent Dimensional Stability
 Suitable for electrical insulation and other general application.  
J-404 co extruded transparent corona treated polyester film having excellent surface and good handling property. And Treated side wound Outside. 75,100,125,190,250 µ
  • Improved Adhesion Properties on Corona Treated Side
  • Good Insulation Property
  • Excellent Machinability
  • Excellent Mechanical Properties
  • Excellent Dimensional Stability
 Suitable for electrical insulation and other general application.  
J-411 J411, co extruded transparent and intermediate hazy polyester film having excellent surface and good handling property. Film is one side chemically treated to enhance adhesion properties. 23,30,75,100 µ
  • Good Transparency
  • Good Insulation Property
  • Excellent Machinability
  • Good Ink Adhesion Property
 Suitable for solvent base ink printing, electrical insulation and other general purpose and industrial application  
J-412 J412, co extruded transparent and intermediate hazy polyester film having excellent surface and good handling property. Film is both side chemically treated to enhance adhesion properties. 23,30,75,100 µ
  • Good Transparency
  • Good Insulation Property
  • Excellent Machinability
  • Good Ink Adhesion Property
 Suitable for solvent base ink printing, electrical insulation and other general purpose and industrial application  

THERMAL GLOSS FINISH BOPP FILM

Application:

• Electrical applications (wire and cable insulation) • General purpose use and other industrial applications

Description:

J-400 grade of polyester film is a hazy and both side untreated bi-axially oriented polyester film.

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
J-400
J-400 grade of polyester film is a hazy and both side untreated bi-axially oriented polyester film.
• Electrical applications (wire and cable insulation) • General purpose use and other industrial applications Hazy and both side untreated bi-axially oriented polyester film

THERMAL GLOSS FINISH BOPP FILM

Application:

Suitable for electrical insulation and other general application.

Description:

co extruded transparent corona treated polyester film having excellent surface and good handling property. And Treated side wound inside.

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
J-403
co extruded transparent corona treated polyester film having excellent surface and good handling property. And Treated side wound inside.
Suitable for electrical insulation and other general application. Eextruded transparent corona treated polyester film having excellent surface and good handling property, J403 is inside and J404 is out side corona

THERMAL GLOSS FINISH BOPP FILM

Application:

Suitable for electrical insulation and other general application.

Description:

co extruded transparent corona treated polyester film having excellent surface and good handling property. And Treated side wound Outside.

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
J-404
co extruded transparent corona treated polyester film having excellent surface and good handling property. And Treated side wound Outside.
Suitable for electrical insulation and other general application. Eextruded transparent corona treated polyester film having excellent surface and good handling property, J403 is inside and J404 is out side corona

THERMAL GLOSS FINISH BOPP FILM

Application:

Suitable for solvent base ink printing, electrical insulation and other general purpose and industrial application

Description:

J411, co extruded transparent and intermediate hazy polyester film having excellent surface and good handling property. Film is one side chemically treated to enhance adhesion properties.

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
J-411
J411, co extruded transparent and intermediate hazy polyester film having excellent surface and good handling property. Film is one side chemically treated to enhance adhesion properties.
Suitable for solvent base ink printing, electrical insulation and other general purpose and industrial application Transparent and intermediate hazy polyester film having excellent surface and good handling property, film is one side chemically treated to enhance adhesion properties

THERMAL GLOSS FINISH BOPP FILM

Application:

Suitable for solvent base ink printing, electrical insulation and other general purpose and industrial application

Description:

J412, co extruded transparent and intermediate hazy polyester film having excellent surface and good handling property. Film is both side chemically treated to enhance adhesion properties.

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
J-412
J412, co extruded transparent and intermediate hazy polyester film having excellent surface and good handling property. Film is both side chemically treated to enhance adhesion properties.
Suitable for solvent base ink printing, electrical insulation and other general purpose and industrial application Transparent and intermediate hazy polyester film having excellent surface and good handling property, film is both side chemically treated to enhance adhesion properties
 

About Us

Applications

Products

Other Links

E-Sales

*Disclosure: Formerly a Division of Jindal Poly Films Limited.

Follow Us On