Transparent Non Heat Sealable

Product Table / Data Sheet

 

Type Description Standard Thickness* (µ) USP Application PDF
N0 Transparent Non Heat Sealable Untreated Release 12 TO 35 µ
  • High Surface Gloss
  • Excellent Antistatic Characteristics
  • Moderate Slip
  • Very Good Smooth Surface for Protecting Scratches on Laminates
  • Untreated Surface for Preventing Sticking Between Laminates
  • Excellent Dimensional Stability
Release Liner for Decorative Laminates  

THERMAL GLOSS FINISH BOPP FILM

Application:

Release Liner for Decorative Laminates

Description:

Transparent Non Heat Sealable Untreated Release

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
N0
Transparent Non Heat Sealable Untreated Release
Release Liner for Decorative Laminates Transparent, Non Heat Sealable, Untreated, High Glossy OPP Film with Excellent Clarity and Antistatic Property for use in Release Lining Application for Decorative Laminate Manufacturing. The surface of the film is specifically designed for providing very easy release between the decorative laminates as well as protecting the laminate surface for developing scratches during crosslinking stage.