JPFL Films Private Limited

Transparent Heat Sealable

Product Table / Data Sheet

 

Type Description Standard Thickness* (µ) USP Application PDF
H1 Transparent Both Side Heat Sealable One Side Corona Treated 15 to 50 µ
  • Excellent Hot-Tack and Seal Strength on Both Sides
  • High Surface Gloss and Transparency
  • Very Good Barrier Properties
  • Excellent Slip and Antistatic Properties
  • Excellent Surface Treatment Retention
  • Excellent Adhesion of Inks and Adhesive on Treated Side
  • Excellent Machinability
  • Excellent Mechanical Properties
  • Excellent Dimensional Stability
 Transparent, both side heat sealable one side corona treated film for single/two ply printing lamination application  
H1-LS Transparent Low Heat Sealable Low COF One Side Corona Treated 15 to 50 µ
  • Low Seal Initiation Temperature
  • Very High Hot-Tack and Seal Strength
  • High Surface Gloss and Transparency
  • Very Good Barrier Properties
  • Excellent Slip and Antistatic Properties
  • Excellent Surface Treatment Retention
  • Excellent Adhesion of Inks and Adhesive on Treated Side
  • Excellent Machinability
  • Excellent Mechanical Properties
  • Excellent Dimensional Stability
 Low Heat Sealable, One Side Corona Treated, Low COF Film for single / two Ply Packaging Structure for High Speed Packaging Applications  
H1-ULS Transparent Ultra Low Heat Sealable Low COF One Side Corona Treated 15 to 50 µ
  • Ultra Low Seal Initiation Temperature
  • Very High Hot-Tack and Seal Strength
  • High Surface Gloss and Transparency
  • Very Good Barrier Properties
  • Excellent Slip and Antistatic Properties
  • Excellent Surface Treatment Retention
  • Excellent Adhesion of Inks and Adhesive on Treated Side
  • Excellent Machinability
  • Excellent Mechanical Properties
  • Excellent Dimensional Stability
 Ultra-Low Heat Sealable, One Side Corona Treated, Low COF Film for single / two Ply Packaging Structure for High Speed Packaging Applications  
H1-UUS Transparent Ultra Ultra Low Heat Sealable Low COF One Side Corona Treated 15 to 50 µ
  • Ultra Ultra Low Seal Initiation Temperature
  • Very High Hot-Tack and Seal Strength
  • High Surface Gloss and Transparency
  • Very Good Barrier Properties
  • Excellent Slip and Antistatic Properties
  • Excellent Surface Treatment Retention
  • Excellent Adhesion of Inks and Adhesive on Treated Side
  • Excellent Machinability
  • Excellent Mechanical Properties
  • Excellent Dimensional Stability
 Ultra Ultra-Low Heat Sealable, One Side Corona Treated, Low COF Film for single / two Ply Packaging Structure for High Speed Packaging Applications  
S1 Transparent One Side Non Heat Sealable Corona Treated Other Side Heat Sealable 18 TO 35 µ
  • Excellent Hot-Tack and Seal Strength on Sealable Side
  • High Surface Gloss and Transparency
  • Very Good Barrier Properties
  • Excellent Slip and Antistatic Properties
  • Excellent Surface Treatment Retention
  • Excellent Adhesion of Inks and Adhesive on Non Sealable Treated Side
  • Excellent Machinability
  • Excellent Mechanical Properties
  • Excellent Dimensional Stability
 Transparent, One Side Non Heat Sealable Corona Treated Other Side Heat Sealable Film for single / two Ply Printing Lamination & Biscuit Inner Wrap Application  

THERMAL GLOSS FINISH BOPP FILM

Application:

Transparent, both side heat sealable one side corona treated film for single/two ply printing lamination application

Description:

Transparent Both Side Heat Sealable One Side Corona Treated

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
H1
Transparent Both Side Heat Sealable One Side Corona Treated
Transparent, both side heat sealable one side corona treated film for single/two ply printing lamination application Transparent, both side Heat Sealable, One Side Corona Treated OPP Film with Excellent Barrier, Clarity, Slip and Antistatic Properties for Single / Two Ply printing laminate application. The Corona treated side is specifically designed for Excellent Adhesion of Inks and Lamination Adhesive during conversion. Both the sides exhibit Excellent hot-tack and Seal Strength.

THERMAL GLOSS FINISH BOPP FILM

Application:

Low Heat Sealable, One Side Corona Treated, Low COF Film for single / two Ply Packaging Structure for High Speed Packaging Applications

Description:

Transparent Low Heat Sealable Low COF One Side Corona Treated

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
H1-LS
Transparent Low Heat Sealable Low COF One Side Corona Treated
Low Heat Sealable, One Side Corona Treated, Low COF Film for single / two Ply Packaging Structure for High Speed Packaging Applications Transparent Low Heat Sealable Low Co-efficient of Friction One Side Corona Treated OPP Film with Excellent Clarity, Slip and Antistatic Properties for Single / Two Ply Laminate for High Speed Packaging Application. The Corona treated side is specifically designed for Excellent Adhesion of Inks and Lamination Adhesive during conversion. Both the sides exhibit very High Hot-tack and Seal Strength.

THERMAL GLOSS FINISH BOPP FILM

Application:

Ultra-Low Heat Sealable, One Side Corona Treated, Low COF Film for single / two Ply Packaging Structure for High Speed Packaging Applications

Description:

Transparent Ultra Low Heat Sealable Low COF One Side Corona Treated

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
H1-ULS
Transparent Ultra Low Heat Sealable Low COF One Side Corona Treated
Ultra-Low Heat Sealable, One Side Corona Treated, Low COF Film for single / two Ply Packaging Structure for High Speed Packaging Applications Transparent Ultra Low Heat Sealable Low Co-efficient of Friction One Side Corona Treated OPP Film with Excellent Clarity, Slip and Antistatic Properties for Single / Two Ply Laminate for High Speed Packaging Application. The corona treated side is specifically designed for excellent adhesion of inks and lamination adhesive during conversion. Both the sides exhibit very high hot-tack and seal strength.

THERMAL GLOSS FINISH BOPP FILM

Application:

Ultra Ultra-Low Heat Sealable, One Side Corona Treated, Low COF Film for single / two Ply Packaging Structure for High Speed Packaging Applications

Description:

Transparent Ultra Ultra Low Heat Sealable Low COF One Side Corona Treated

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
H1-UUS
Transparent Ultra Ultra Low Heat Sealable Low COF One Side Corona Treated
Ultra Ultra-Low Heat Sealable, One Side Corona Treated, Low COF Film for single / two Ply Packaging Structure for High Speed Packaging Applications Transparent Ultra Ultra Low Heat Sealable Low Co-efficient of Friction One Side Corona Treated OPP Film with Excellent Clarity, Slip and Antistatic Properties for Single / Two Ply Laminate for High Speed Packaging Application. The corona treated side is specifically designed for excellent adhesion of inks and lamination adhesive during conversion. Both the sides exhibit very high hot-tack and seal strength

THERMAL GLOSS FINISH BOPP FILM

Application:

Transparent, One Side Non Heat Sealable Corona Treated Other Side Heat Sealable Film for single / two Ply Printing Lamination & Biscuit Inner Wrap Application

Description:

Transparent One Side Non Heat Sealable Corona Treated Other Side Heat Sealable

Salient Features:

Typical values

Product Code Micron Description Layers Application Application Description Salient Features Thickness Grammage Yield Treatment Level 1 Treatment Level 2 Wetting Tension (Plainl) Wetting Tension (Coated Side) Wetting Tension (Corona Side) Treatment level ( Coated side) Treatment level (PVdC coated side) Treatment level ( Acrylic side) Treatment level (Plain side) Treatment level (Corona side) Treatment level (Metal side) Treatment level (Other side) Optical Densityl (Min) Metal Bond Strength COF Max (Untreated/Untreated) Max COF Max Ato B (oppostive Surfces) Max 1 COF Max Ato B (oppostive Surfces) Max 2 COF (Coated/uncoated) COF (Acrylic/Acrylic) COF (PVdC/PVdC) COF (coated/metal) COF (uncoated/metal) Haze Gloss at 60 Tensile Strength (MD) Min Tensile Strength (TD) Min Modulus (MD) Modulus (TD) Elongation (MD) Min Elongation (TD) Min Shrinkage (150°C/30min) MD Max Shrinkage (150°C/30min) TD Max Shrinkage (190°C/20min) MD Max Shrinkage (190°C/20min) TD Max Water Vapour Transmission Rate Oxygen Gas Transmission Rate BDV (KV) Volume Resistivity Surface Resistivity Opacity Min Ratio OF TS (+450/-450) Wettability (min) Coefficient of Friction Elongation at break MD Elongation at break TD Seal strength VTR (38°C & 90% RH) OTR (23°C & 0% RH) Antifog (Hot) Antifog (Cold) Heat Seal Range Treatment at Extrusion coated side – min. Treatment at Uncoated Matte side – min. Gloss – Uncoated Matte side (at 45°) Lamination temperature Seal strength(Acrylic/Acrylic) @130ºC/2 Bar /1 Sec (min) Seal strength(Acrylic/Acrylic) @140ºC/2 Bar /1 Sec (min) Seal strength(PVdC/ PVdC) @140ºC/2 Bar /1 Sec (min) Silicon Rub-off Release force(Tesa tape -7475, @300 mm/min, 180° peeling)
PHYSICAL
S1
Transparent One Side Non Heat Sealable Corona Treated Other Side Heat Sealable
Transparent, One Side Non Heat Sealable Corona Treated Other Side Heat Sealable Film for single / two Ply Printing Lamination & Biscuit Inner Wrap Application Transparent, One Side Heat Sealable, One Side Corona Treated OPP Film with Excellent Barrier, Clarity, Slip and Antistatic Properties for Single / Two Ply Printing Lamination & Biscuit Inner Wrap Application. The corona treated side is specifically designed for excellent adhesion of inks and lamination adhesive during conversion. Both the sides exhibit excellent hot-tack and seal strength
 

About Us

Applications

Products

Other Links

E-Sales

*Disclosure: Formerly a Division of Jindal Poly Films Limited.

Follow Us On